The item is packaged in a 2 gram rigid plastic tube separated by a leak-proof clamp (BIPAX). Remove the clamp and mix right inside the BIPAX. This eliminates mix ratio errors with pre-measured resin and catalyst components.This package will prepare approximately 25~30 connectors. High Tg and Room Temperature Curing Fiber Optic Epoxy Adhesive TRA-BOND F113SC is a room temperature curing, high Tg and low viscosity adhesive formulated for terminating ALL TYPES of fiber optic connectors. It has also been used for bonding LED displays, lenses and other optical components. TRA-BOND F113SC provides both high bond strength as well as low stress connections with no pistoning. This two part system can be cured overnight at room temperature or as quickly as 15 minutes at 9°C and is provided in a dark blue color to allow for easy polishing. Please Note: Ground Shipment Only Features: 2-Part, 2.5-Gram Bi-Pack Heat/Time Cure, 30mins - 24Hrs @ Room Temp to 80°C Blue Dye Epoxy 45 minute Pot Life in a Syringe Singlemode / Multimode Applications Properties Color, resin Clear Color, hardener Dark Blue Color, mixed Dark Blue Specific gravity, mixed 1.1 Index of refraction 1.52 Viscosity, cps, mixed ((after mixing) @ 2°C) 1800 Thixotropic index 1 Operating temperature range,°C -60/120 Hardness, Shore D 83 Mix ratio, pbw, Resin/Hardener 100/30 Lap shear, alum to alum, psi (1 hour @ 6°C) 3900 Lap shear, alum to alum, psi (24 hours @ 2°C) 2700 Glass transition (Tg),°C, ultimate 95 Water absorption, % 0.98 VOC, grams/l 1.91 Coefficient of expansion, cm/cm°C (above Tg) 0.000191 Coefficient of expansion, cm/cm°C (below Tg) 0.0000757 Cure Schedule 18 hours @ 2°C or 1 hour @ 6°C or 15 minutes @ 9°C for one drop applications Material Safety Data Sheet Download MSDS from here. Tech Sheet