Bambu PLA-CF Bambu PLA-CF is carbon fiber reinforced PLA with improved stiffness and strength. PLA-CF is easy to print and beginner-friendly like regular PLA. It is AMS compatible with low clogging risk at high-speed printing. The prints are in matte finish with almost invisible layer lines, which make it suitable for printing general engineering parts or models requiring a better appearance, like bike frames, brackets and toys. Carbon fiber texture & Minimized layer lines The addition of carbon fiber gives prints a unique matte finish and effectively hides layer lines, providing a smooth, premium look. Display of Prints Bambu PLA-CF could be paired with any PLA series filament to make your prints more colorful and achieve various texture requirements. Improved mechanical properties Bambu PLA-CF exceeds the mechanical properties of PLA Matte in XY Bending Strength, Z Bending Strength, XY Bending Modulus, Z Bending Modulus, XY Impact Strength, and Z Impact Strength by between 20% and 115%, making it more suitable for printing models with higher strength requirements. Mechanical Properties Comparison PLA Matte PLA-CF Improved % Tensile Strength - XY/MPa 32 38 19% Tensile Strength - Z/MPa 25 26 4% Bending Strength - XY/MPa 53 89 68% Bending Strength - Z/MPa 32 49 53% Bending Modulus - XY/MPa 2360 3950 67% Bending Modulus - Z/MPa 2040 2260 10% Impact Strength - XY/(kJ/m²) 19.2 23.2 20% Impact Strength - Z/(kJ/m²) 6.6 7.8 18% *Drying PLA is recommended for humid environments at 55 °C for 8 hours before printing. Stablized printing dimension Bambu PLA-CF features low shrinkage and warping resistance to achieve a perfect matching accuracy between prints parts. Minimal effort in support removal Bambu PLA-CF is designed to support itself. It can be removed more easily compared to regular PLA, and still maintains a smooth support surface. Not prone to clogging in high-speed printing Bambu PLA-CF is just as easy to print as regular PLA. It can be printed smoothly and consistently at high speed without clogging. Accessory Compatibility Recommended Not Recommended Build Plate Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate / Hotend Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm Hotend with Stainless Steel Nozzle All Size Glue Bambu Liquid GlueGlue Stick / PLA-CF Hex Code Table Color Hex Code Display Burgundy Red #951e23 Matcha Green #5c9748 Jeans Blue #6e88bc Royal Blue #2842AD Iris Purple #69398E Lava Gray #4d5054 Black #000000 RFID for Intelligent Printing All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps. Parameters Comparison Learn more different filaments comparison on Bambu Filament Guide >> PETG-CF PLA-CF Price $34.99 $34.99 Filament Type Carbon Fiber Infill Carbon Fiber Infill Hotend Compatibility Hardened Steel (0.4, 0.6, 0.8 mm) Hardened Steel (0.4, 0.6, 0.8 mm) Build Plate Compatibility Engineering Plate, High Temperature Plate, Textuerd PEI Plate Cool Plate, High Temperature Plate, Textuerd PEI Plate AMS Compatibility Yes Yes Surface Shiny Matte Print Speed < 200 mm/s < 200 mm/s Toughness (Impact Strength - XY) 41.2 kJ/m² 23.2 kJ/m² Strength (Bending Strength - XY) 70 MPa 89 MPa Stiffness (Bending Modulus - XY) 2910 MPa 3950 MPa Layer Adhesion (Impact Strength - Z) 10.7 kJ/m² 7.8 kJ/m² Heat Resistant（HDT, 0.45 MPa） 74 °C 55 °C Recommended Printing Settings Drying Settings (Blast Drying Oven) 55 °C, 8 h Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant) Nozzle Temperature 210 - 240 °C Bed Temperature (with Glue) 35 - 45 °C Printing Speed < 200 mm/s Physical Properties Density 1.22 g/cm³ Vicat Softening Temperature 69 °C Heat Deflection Temperature 55 °C Melting Temperature 165 °C Melt Index 3.7 ± 0.6 g/10 min Mechanical Properties Tensile Strength 38 ± 4 MPa Breaking Elongation Rate 8.4 ± 3.2 % Bending Modulus 3950 ± 190 MPa Bending Strength 89 ± 4 MPa Impact Strength 23.2 ± 3.7 kJ/m²
Related
Related
Related
Related