Hydrophobic Graphite Double-Side Coated on Copper Foil as Aqueous Li-Ion Battery Anode - (241mm L x 200mm W x 90um Thick), 5 sheets/bag, bccf-241-ds-h

MTI Online Store Verified independent store

→

This electrode sheet is based on copper foil coated by graphite in the double sides, and it is mainly used as an aqueous Li-Ion battery anode with hydrophobic surface feature. Spec ifications Current collector (substrate): Copper foil, 9 micron Anode material: Artificial Graphite (95.5%) Binder: PVDF (3%), conductive carbon" Super P, 1.5% Compaction density: 1.25 g/cm3 Double sides coating material density: 12.6 mg/c㎡ Length: 241mm, Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating) Total Thickness: 90 um +/- 8 um Foil Thickness: 10 um +/- 3 um Coating Thickness:80 um +/- 5 um (double side coated) ( 40 micron on each side ) Specific Capacity: 300mAh/g Qty: 5 Sheets/bagWarning: Please dry in vacuum oven before using and store it inside the glovebox after opening the package. The recommended temperature and time can be 80-120 °C for 6-12h. Note: if you use the electrode sheet for single layer button cell, you shall remove one layer coating with sandpaper to make one side contact to the button cell case. How to make a water-based electrode (graphite for the anode) for your reference: 1. Weight Ratio (All other weights depends on how much active power your will use): Active Powder: 92.5% CMC: 1.5% SBR liquid: 2.5% Conductive: 3.5% Absolute Alcohol: 15ml/kg graphite DI water: At least 125% of graphite 2. Make liquid thicken agent: Heat up Deionized water to 60C and then slowly put the CMC into it and keep stirring unless all of them dissolved. 3. Put alcohol into 125% Deionized water and then to conductive powder to stir. 4. Put active powder into 3 and stir (better have vacuum mixing) 5. Put liquid thicken agent into 4 and stir (better have vacuum mixing) 6. Put SBR into 5 and stir (better have vacuum mixing) 7. Take a little sample and test the viscosity, if, in 3000-5000 mPa·s, it is OK to coat, if over, put some Deionized water, if less, the binder in (CMC and SBR) Click below to view the video: how to coat the electrode and then make a coin cell Related Products Vacuum Storage Box Powder Milling & Mixer Electrode Coaters Battery Research Equipment Other Battery Powder Solid Electrolyte Show more