Nickel Foam (200mm length x 300mm width x 1.6mm thickness) - bcnf-16m2

MTI Online Store Verified independent store

→

Specifications Material: Nickel Foam, Purity> 99.99% (excellent anti-corrosive) Surface Density: 346g/m^2 Length: 200 mm ± 0.5 mm Width: 300mm ± 0.5 mm Thickness: 1.6 mm ± 0.5 mm N et weight: 21g Porosity: ≥95% (80-110 Pores per Inch, average hole diameters about 0.25mm) Extensibility: Lengthwise≥5%; Widthwise≥12% Tensile StrengthLengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2: Young’s Modulus: 200 MPa Thermal Conductivity: 90.9 W/m·K Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel. How to clean the Nickel Foam for Battery Cathode Substrate. NiO can be removed by annealing in the hydrogen furnace. Nickel foam (about 3.3 cm x 1 cm) was carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned. MSDS DOWNLOAD Porosity: ≥95% (80-110 Pores per Inch, average hole diameter is about 0.25mm Click the video above to see the battery cathode coated by MTI's Film coater MSK-AFA-II-VC Other Metallic Foams Related Product Battery Powders Heatable Ultrasonic Cleaner Electrode Coating Coin Cell Assembling Pouch Cell Assembling Cylinder Cell Assembling Electrolyte injection Show more