QIDI PETG-CF QIDI PETG-CF Filament: Strong, Rigid & Easy to Print, It combines the ease of use of PETG with the strength of carbon fiber, resulting in prints that are significantly more rigid, sturdy, and resistant to bending. It offers excellent dimensional stability, precise details, and a premium matte textured finish. Enhanced Heat & Chemical Resistance This material inherits PETG's excellent resistance to most oils, greases, and detergents. Its heat deflection temperature is slightly higher than that of standard PETG, allowing it to be used in higher temperature environments. High Strength & Stiffness The printed parts are stronger and harder than ordinary PETG or PLA, approaching the performance of some engineering plastics. 150mm/s High-Speed Printing Say goodbye to long waits! PETG-CF supports high-speed printing at 150mm/s, helping you take the manufacturing efficiency of high-strength parts to a new level and achieve twice the result with half the effort. Matte, Industrial Finish The carbon fiber gives the finished product a unique matte, frosted texture with a subtle grain texture on the surface, making the appearance more "industrial" and high-end. Easy to Print & Beginner-Friendly Adding chopped carbon fiber provides greater dimensional stability and low shrinkage, increasing the success rate of printing large models. Equipped with RFID chip Equipped with RFID chip, parameters are automatically identified, saying goodbye to manual settings. Accessory Compatibility Recommended Not Recommended Multi-color printing system QIDI BOX / Support Filaments PLA Basic / Build Plate QIDI PEI Plate, QIDI Smooth Plate, QIDI Cool Plate, HF Plate, PC Plate / Nozzle Hardened Steel Nozzle (0.4 / 0.6mm) Bimetal Nozzle (0.4 / 0.6/0.8mm) Tungsten Carbide Bimetal Nozzle (0.4 / 0.6/0.8mm) Brass/Copper plated Nozzle (0.2/0.4 / 0.6/0.8mm) Any 0.2mm size Nozzle Recommended Printing Settings Drying Settings (Blast Drying Oven) 65 °C，5-8 h Nozzle Temperature 240-270 °C Bed Temperature 70-80 °C Printing Speed 20-150 mm/s Physical Properties Density 1.31 g/cm³ Melt Flow Rate 8~14g/10min Vicat Softening Temperature 83°C Heat Deflection Temperature 77℃ Mechanical Properties Tensile Strength(X-Y) 57 MPa Tensile Modulus (X-Y) 3700 MPa Elongation at Break (X-Y) 7 % Impact Strength (X-Y) 30 KJ/m² Downloads Filament TDS Filament MSDS Printing Tips Pre-printing Drying: PETG-CF is highly hygroscopic.Moist filament may cause stringing and reduced strength during printing.It is recommended to dry at 65°C for 5-8 hours.For extended prints, using a dry box or continuous drying during printing is advised. Nozzle Recommendation: The glass fiber content is highly abrasive and can quickly wear down standard brass nozzles, leading to nozzle enlargement and extrusion inaccuracies.A hardened steel nozzle or harder is recommended. 📚For more details please refer to: Filament Guide on WIKI. Vacuum Aluminum Foil Packaging According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant. Product Size QIDI TECH PETG-CF Filament 1.75mm Works perfectly with most FDM 3Dprinters on the market.
