QIDI PPS-GF20 Born to tackle the most demanding engineering challenges. PPS-GF20, combining exceptional heat resistance, outstanding dimensional stability, and top-tier electrical insulation properties, is your ultimate choice for achieving innovation and reliability in electronics, aerospace, automotive manufacturing, and high-end industrial applications. Flame-retardant and chemically resistant UL94 V0 certified at a thickness of 1.5mm, resistant to acids, alkalis, oils, and solvents. Chemical Resistance of PPS-GF Material Category Excellent Resistance Limited Resistance / Not Recommended Acids ✅ Acids Hydrochloric acid, phosphoric acid, acetic acid, etc. ⚠️ Strong oxidizing acids Nitric acid, hot concentrated sulfuric acid, chromic acid Alkalis ✅ Alkalis Sodium hydroxide, potassium hydroxide, ammonia water ⚠️ Certain strong polar solvents Nitrobenzene, aniline Solvents ✅ Solvents Alcohols, ketones, esters, hydrocarbons, halogenated hydrocarbons Oils & Lubricants ✅ Oils, fuels, lubricants Water & Steam ✅ Hot water and steam Excellent Insulation Performance Boasting a high dielectric strength of 6.1 kV/mm and a low dielectric constant (2.7 @ 1MHz), it provides a solid protective barrier for applications such as 5G base station components, ADAS sensor housings, and electrical insulators. Exceptional High-Temperature Resistance Maintains excellent structural strength and shape even in extreme environments up to 240°C (Heat Deflection Temperature). High Strength and Rigidity Filled with 20% glass fiber, it reduces material shrinkage while providing printed parts with strength and rigidity (Young's modulus up to 4600 MPa, XY flexural strength up to 105 MPa). Especially suitable for brackets, antenna bases, chemical contact parts, and other components with stringent requirements for strength and stiffness. Precision, Reliability, and Easy Printing Supports high-speed printing . Extremely low shrinkage and excellent dimensional stability ensure printed parts maintain precise dimensions from the first layer to the last, enabling easy creation of tightly fitting assemblies and high-precision gear sets. Ultra-Low Water Absorption PPS-GF exhibits an extremely low moisture absorption rate of just 0.05%, maintaining stable mechanical and thermal properties even in humid environments. This makes it an ideal choice for high-moisture resistance applications. Equipped with RFID chip Equipped with RFID chip, parameters are automatically identified, saying goodbye to manual settings. Accessory Compatibility Category Recommended Not Recommended Multi-color printing system QIDI BOX / Build Plate QIDI PEI Plate, QIDI Smooth Plate, QIDI Cool Plate, HF Plate, PC Plate / Nozzle Hardened Steel Nozzle (0.4 / 0.6mm) Bimetal Nozzle (0.4 / 0.6/0.8mm) Tungsten Carbide Bimetal Nozzle (0.4 / 0.6/0.8mm) Brass/Copper plated Nozzle (0.2/0.4 / 0.6/0.8mm) Any 0.2mm size Nozzle Recommended Printing Settings Drying Settings (Blast Drying Oven) 100 °C，8-10 h Nozzle Temperature 300-350 °C Bed Temperature 80-100 °C Printing Speed 20-150 mm/s Physical Properties Density 1.36 g/cm³ Melt Flow Rate 27 g/10min Vicat Softening Temperature 272.5°C Heat Deflection Temperature 236.3°C Mechanical Properties Tensile Strength(X-Y) 64.1±2.1 MPa Tensile Modulus (X-Y) 4552.0±54.6 MPa Elongation at Break (X-Y) 2.0±0.2% Impact Strength (X-Y) 27.3±1.1 kJ/㎡ Downloads Filament TDS Filament MSDS Printing Tips Equipment Requirements: The hot end operating temperature must be set between 310°C and 350°C . Higher temperatures result in greater filament strength, but print quality will decrease with increasing temperature. Hardened steel or higher-grade nozzles are recommended to withstand fiberglass abrasion. Material Handling: Ensure the filament is thoroughly dried before printing to prevent print failure. To prevent moisture absorption, use a sealed storage container with a desiccant during printing. When not in use, the material must be sealed and stored in a dry environment. Post-Processing: Annealing the printed parts can significantly improve their mechanical properties and thermal stability. However, some prints may warp or deform, especially larger or thinner prints. Recommended annealing conditions: 130°C for 10 hours. QIDI BOX Usage Tips: Since this filament uses a cardboard spool, it is recommended to use a spool adapter (ABS Filament is recommended) on the cardboard spool when printing this filament with QIDI BOX to prevent the spool from being unable to rotate during material ejection. 📚For more details please refer to: Engineering Filament Guide on WIKI. Vacuum Aluminum Foil Packaging According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant. Product Size QIDI TECH PPS-GF20 Filament 1.75mm Works perfectly with most FDM 3Dprinters on the market.
Related
Related
Related
Related